High-capacity nickel-rich layered oxides are promising cathode materials for high-energy-density lithium batteries. However, the poor structural stability and severe side reactions at the electrode/electrolyte interface result in unsatisfactory cycle performance. Herein, the thin layer of two-dimensional (2D) graphitic carbon-nitride (g-C3N4) is uniformly coated on the LiNi0.8Co0.1Mn0.1O2 (denoted as NCM811@CN) using a facile chemical vaporization-assisted synthesis method. As an ideal protective layer, the g-C3N4 layer effectively avoids direct contact between the NCM811 cathode and the electrolyte, preventing harmful side reactions and inhibiting secondary crystal cracking. Moreover, the unique nano-pore structure and abundant nitrogen vacancy edges in g-C3N4 facilitate the adsorption and diffusion of lithium ions, which enhances the lithium deintercalation/intercalation kinetics of the NCM811 cathode. As a result, the NCM811@CN-3wt% cathode exhibits 161.3 mAh g-1 and capacity retention of 84.6% at 0.5 C and 55 °C after 400 cycles and 95.7 mAh g-1 at 10 C, which is greatly superior to the uncoated NCM811 (i.e. 129.3 mAh g-1 and capacity retention of 67.4% at 0.5 C and 55 °C after 220 cycles and 28.8 mAh g-1 at 10 C). The improved cycle performance of the NCM811@CN-3wt% cathode is also applicable to solid-liquid-hybrid cells composed of PVDF:LLZTO electrolyte membranes, which show 163.8 mAh g-1 and the capacity retention of 88.1% at 0.1 C and 30 °C after 200 cycles and 95.3 mAh g-1 at 1 C.

Zinc metal anodes are gaining popularity in aqueous electrochemical energy storage systems for their high safety, cost-effectiveness, and high capacity. However, the service life of zinc metal anodes is severely constrained by critical challenges, including dendrites, water-induced hydrogen evolution, and passivation. In this study, a protective two-dimensional metal-organic framework interphase is in situ constructed on the zinc anode surface with a novel gel vapor deposition method. The ultrathin interphase layer (~1 µm) is made of layer-stacking 2D nanosheets with angstrom-level pores of around 2.1 Å, which serves as an ion sieve to reject large solvent-ion pairs while homogenizes the transport of partially desolvated zinc ions, contributing to a uniform and highly reversible zinc deposition. With the shielding of the interphase layer, an ultra-stable zinc plating/stripping is achieved in symmetric cells with cycling over 1000 h at 0.5 mA cm-2 and ~700 h at 1 mA cm-2, far exceeding that of the bare zinc anodes (250 and 70 h). Furthermore, as a proof-of-concept demonstration, the full cell paired with MnO2 cathode demonstrates improved rate performances and stable cycling (1200 cycles at 1 A g-1). This work provides fresh insights into interphase design to promote the performance of zinc metal anodes.

We employ advanced first-principles methodology, merging self-consistent phonon theory and the Boltzmann transport equation, to comprehensively explore the thermal transport and thermoelectric properties of KCdAs. Notably, the study accounts for the impact of quartic anharmonicity on phonon group velocities in the pursuit of lattice thermal conductivity and investigates 3ph and 4ph scattering processes on phonon lifetimes. Through various methodologies, including examining atomic vibrational modes and analyzing 3ph and 4ph scattering processes, the paper unveils microphysical mechanisms contributing to the low $\kappa_{L}$ within KCdAs. Key features include significant anisotropy in Cd atoms, pronounced anharmonicity in K atoms, and relative vibrations in non-equivalent As atomic layers. Cd atoms, situated between As layers, exhibit rattling modes and strong lattice anharmonicity, contributing to the observed low $\kappa_{L}$. Remarkably flat bands near the valence band maximum translate into high PF, aligning with ultra-low $\kappa_{L}$ for exceptional thermoelectric performance. Under optimal temperature and carrier concentration doping, outstanding \textit{ZT} values are achieved: 4.25 (a(b)-axis, p-type), 0.90 (c-axis, p-type), 1.78 (a(b)-axis, n-type), and 2.36 (c-axis, n-type).

Skin-like electronics research aiming to mimic even surpass human-like specific tactile cognition by operating perception-to-cognition-to-feedback of stimulus to build intelligent cognition systems for certain imperceptible or inappreciable signals was so attractive. Herein, we constructed an all-in-one wearable device to address the sensitivity and power supply simultaneously by integrating multistage micro-structured ionic skin (MM i-skin) and piezoelectric & thermoelectric dual-mode self-power staffs. The MM i-skin with multi-stage “interlocked” configurations achieved precise recognition of subtle signals, where the sensitivity reached up to 77.4 kPa-1, as well as response time of 46 ms, cyclic stability (over 1500 cycles), and a pressure detection limit (over 50 kPa). Furthermore, we developed a piezo/thermo-electricity dual-mode nanogenerator, denoted as P-iskin / T-iskin, for self-powering the pressure sensor. This self-powered multifunctional ionic skin enables real-time monitoring of weak body signals, rehab guidance, and robotic motion recognition, demonstrating potential for internet of things (IoT) applications involving the artificial intelligence-motivated sapiential healthcare internet (SHI) and widely distributed human-machine interaction (HMI).

Heterogeneous catalysts promoting efficient production of reactive species and dynamically stabilized electron transfer mechanisms for peroxomonosulfates (PMS) still lack systematic investigation. Herein, a more stable magnetic layered double oxides (CFLDO/N-C), was designed using self-polymerization and high temperature carbonization of dopamine. The CFLDO/N-C/PMS system effectively activated PMS to remove 99% (k=0.737 min-1) of tetracycline (TC) within 10 min. The CFLDO/N-C/PMS system exhibited favorable resistance to inorganic anions and natural organics, as well as satisfactory suitability for multiple pollutants. The magnetic properties of the catalyst facilitated the separation of catalysts from the liquid phase, resulting in excellent reproducibility and effectively reducing the leaching of metal ions. An electronic bridge was constructed between cobalt (the active platform of the catalyst) and PMS, inducing PMS to break the O-O bond to generate the active species. The combination of static analysis and dynamic evolution confirmed the effective adsorption of PMS on the catalyst surface as well as the strong radical-assisted electron transfer process. Eventually, we further identified the sites where the reactive species attacked the TC and evaluated the toxicity of the intermediates. These findings offer innovative insights into the rapid degradation of pollutants achieved by transition metals in SR-AOPs and its mechanistic elaboration.

Cubic silicon carbide (3C-SiC) has superior mobility and thermal conduction than that of widely applied hexagonal 4H-SiC. Moreover, much lower concentration of interfacial traps between insulating oxide gate and 3C-SiC helps fabricate reliable and long-life devices like metal-oxide-semiconductor field effect transistors (MOSFETs). However, the growth of high quality and wafer-scale 3C-SiC crystals has remained a big challenge up to now despite of decades-long efforts by researchers because of its easy transformation into other polytypes during growth, limiting the development of 3C-SiC based devices. Herein, we report that 3C-SiC can be made thermodynamically favored from nucleation to growth on a 4H-SiC substrate by top-seeded solution growth technique (TSSG), beyond what’s expected by classic nucleation theory. This enables the steady growth of high-quality and large-size 3C-SiC crystals (2~4-inch in diameter and 4.0~10.0 mm in thickness) sustainable. The as-grown 3C-SiC crystals are free of other polytypes and have high crystalline quality. Our findings broaden the mechanism of hetero-seed crystal growth and provide a feasible route to mass production of 3C-SiC crystals, offering new opportunities to develop power electronic devices potentially with better performances than those based on 4H-SiC.

SnO2, with its high theoretical capacity, abundant resources, and environmental friendliness, is widely regarded as a potential anode material for lithium-ion batteries (LIBs). Nevertheless, the coarsening of the Sn nanoparticles impedes the reconversion back to SnO2, resulting in low coulombic efficiency and rapid capacity decay. In this study, we fabricated a heterostructure by combining SnO2 nanoparticles with MoS2 nanosheets via plasma-assisted milling. The heterostructure consists of in-situ exfoliated MoS2 nanosheets predominantly in 1T phase, which tightly encase the SnO2 nanoparticles through strong bonding. This configuration effectively mitigates the volume change and particle aggregation upon cycling. Moreover, the strong affinity of Mo, which is the lithiation product of MoS2, toward Sn plays a pivotal role in inhibiting the coarsening of Sn nanograins, thus enhancing the reversibility of Sn to SnO2 upon cycling. Consequently, the SnO2/MoS2 heterostructure exhibits superb performance as an anode material for LIBs, demonstrating high capacity, rapid rate capability, and extended lifespan. Specifically, discharged/charged at a rate of 0.2 A g-1 for 300 cycles, it achieves a remarkable reversible capacity of 1173.4 mAh g-1. Even cycled at high rates of 1.0 and 5.0 A g-1 for 800 cycles, it still retains high reversible capacities of 1005.3 and 768.8 mAh g-1, respectively. Moreover, the heterostructure exhibits outstanding electrochemical performance in both full LIBs and sodium-ion batteries.

The development of self-charging supercapacitor power cells (SCSPCs) has profound implications for smart electronic devices used in different fields. Here, we epitaxially electrodeposited Mo- and Fe-codoped MnO2 films on piezoelectric ZnO nanoarrays (NAs) grown on the flexible carbon cloth (denoted ZnO@Mo-Fe-MnO2 NAs). An SCSPC device was assembled with the ZnO@Mo-Fe-MnO2 NA electrode and poly(vinylidenefluoride-co-trifluoroethylene) (PVDF-Trfe) piezoelectric film doped with BaTiO3 (BTO) and carbon nanotubes (CNTs) (denoted PVDF-Trfe/CNTs/BTO). The SCSPC device exhibited an energy density of 30 μWh cm-2 with a high-power density of 40 mW cm-2, and delivered an excellent self-charging performance of 363 mV (10 N) driven by both the piezoelectric ZnO NAs and the PVDF-Trfe/CNTs/BTO films. More intriguingly, the device also could also be self-charged by 184 mV due to residual stress alone, and showed excellent energy conversion efficiency and low self-discharge rate. This work illustrates for the first time the self-charging mechanism involving electrolyte ion migration driven by both electrodes and films. A comprehensive analysis strongly confirmed the important contribution of the piezoelectric ZnO NAs in the self-charging process of the SCSPC device. This work provides novel directions and insights for the development of SCSPCs.

The emergence of polymerized small molecule acceptors (PSMAs) has significantly improved the performance of all-polymer solar cells (all-PSCs). However, the pace of device engineering lacks behind that of materials development, so that a majority of the PSMAs have not fulfilled their potentials. Furthermore, most high-performance all-PSCs rely on the use of chloroform as the processing solvent. For instance, the recent high-performance PSMA named PJ1-γ, with high LUMO and HOMO levels, could only achieve a PCE of 16.1% with a high-energy-level donor (JD40) using chloroform. Herein, we present a methodology combining sequential processing (SqP) with the addition of 0.5%wt PC71BM as a solid additive (SA) to achieve an impressive efficiency of 18.0% for all-PSCs processed from toluene, an aromatic hydrocarbon solvent. Compared to the conventional blend-casting (BC) method whose best efficiency (16.7%) could only be achieved using chloroform, the SqP method significantly boosted the device efficiency using toluene as the processing solvent. In addition, the donor we employ is the classic PM6 that has deeper energy levels than JD40, which provides low energy loss for the device. We compare the results with another PSMA (PYF-T-o) with the same method. Finally, an improved photostability of the SqP devices with the incorporation of SA is demonstrated.

Manufacturing thin-film components is crucial for achieving high-efficiency and high-power thermal batteries (TBs). However, developing binders with low gas production at the operating temperature range of TBs (400−550 °C) has proven to be a significant challenge. Here we report the use of acrylic acid derivative terpolymer (LA136D) as a low-volatile binder for thin-film cathode fabrication and studied the chain scission and chemical bond-breaking mechanisms in pyrolysis. It is shown LA136D defers to random-chain scission and cross-linking chain scission mechanisms, which gifts it with a low proportion of volatile products (ψ, ψ=39.2wt%) at even up to 550 °C, well below those of the conventional PVDF (77.6wt%) and SBR (99.2wt%) binders. Surprisingly, LA136D contributes to constructing a thermal shock-resistant cathode due to the step-by-step bond-breaking process. This is beneficial for the overall performance of TBs. In a 130 s pulse discharging test, the thin-film cathodes exhibited a remarkable 440% reduction in polarization and 300% enhancement in the utilization efficiency of cathode materials, while with just a slight increase of 0.05 MPa in gas pressure compared with traditional “thick-film” cathode. Our work highlights the potential of LA136D as a low-volatile binder for thin-film cathodes and shows the feasibility of manufacturing high-efficiency and high-power TBs through polymer molecule engineering.

Solar steam generation is a promising water purification technology due to its low-cost and environmentally friendly applications in water purification and desalination. However, hydrophilic or hydrophobic materials alone are insufficient in achieving necessary characteristics for constructing high-quality solar steam generators with good comprehensive properties. Herein, novel hydrophile/hydrophobe amphipathic Janus nanofibers aerogel is designed and used as a host material for preparing solar steam generators. The product consists of an internal cubic aerogel and an external layer of photothermal materials. The internal aerogel is composed of electrospun amphipathic Janus nanofibers. Owing to the unique composition and structure, the prepared solar steam generator integrates the features of high water evaporation rate (2.944 kg·m-2·h-1 under 1 kW m-2 irradiation), self-floating, salt-resisting, and fast performance recovery after flipping. Moreover, the product also exhibits excellent properties on desalination and removal of organic pollutants. Compared with traditional hydrophilic aerogel host material, the amphipathic Janus nanofibers aerogel brings much higher water evaporation rate and salt resistance.

To unlock the full potential of PSCs, machine learning (ML) was implemented in this research to predict the best combination of mesoporous-titanium dioxide (mp-TiO2) and weight percentage (wt%) of phenyl-C61-butyric acid methyl ester (PCBM), along with the current density (Jsc), open-circuit voltage (Voc), fill factor (ff) and energy conversion efficiency (ECE). Then, the combination that yielded the highest predicted ECE was selected as a reference to fabricate PCBM-PSCs with nanopatterned TiO2 layer. Subsequently, the PCBM-PSCs with nanopatterned TiO2 layers were fabricated and characterized to further understand the dual effects of nanopatterning depth and wt% of PCBM on PSCs. Experimentally, the highest ECE of 17.336% is achieved at 127 nm nanopatterning depth and 0.10 wt% of PCBM, where the Jsc, Voc and ff are 22.877 mA/cm2, 0.963 V and 0.787, respectively. The measured Jsc, Voc, ff and ECE values show consistencies with the ML prediction. Hence, these findings not only revealed the potential of ML to be used as a preliminary investigation to navigate the research of PSCs, but also highlighted that nanopatterning depth has a significant impact on Jsc, and the incorporation of PCBM on perovskite layer influenced the Voc and ff, which further boosted the performance of PSCs.

Due to poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) is water-processable, thermally stable and highly conductive, PEDOT:PSS and its composites have been considered to be one of the most promising flexible thermoelectric materials. However, the PEDOT:PSS film prepared from its commercial aqueous dispersion usually has quite low conductivity, thus cannot be directly utilized for thermoelectric applications. Here, a simple environmentally friendly strategy via femtosecond laser irradiation without any chemical dopants and treatments was demonstrated. Under optimal conditions, the electrical conductivity of the treated film is increased to 803.1 S/cm from 1.2 S/cm around three order of magnitude higher, and the power factor is improved to 19.0 μW·m-1·K-2, which is enhanced more than 200 times. The mechanism for such remarkable enhancement was attributed to the transition of the PEDOT chains from a coil to a linear or expanded coil conformation, reduction of the interplanar stacking distance, and the removal of insulating PSS with increasing the oxidation level of PEDOT, facilitating the charge transportation. This work presents an effective route for fabricating high-performance flexible conductive polymer films and wearable thermoelectric devices.

In this work, a modified polyurethane adhesive (PUA) was prepared to realize a convenient encapsulation strategy for lead efficient sedimentation and for attachable perovskite solar cells (PSCs). The modified PUA can completely self-healing within 45 minutes at room temperature and it has a lead ion blocking rate of 99.3% in the dripping experiment. The PUA film can directly contact with the metal electrode surface with a slight efficiency improvement from 23.96% to 24.15%. The thermal stability of 65℃ and humidity stability of 55% RH is superior to the encapsulated devices with polyisobutylene. The PUA film has strong adhesion to flexible substrate, and the initial efficiency of flexible perovskite module (17.2%) encapsulated by PUA remains 92.6% within 1825 h. These results suggest PUA encapsulation route is universal for rigid and flexible PSCs with enhanced stability and low lead hazardous. Moreover, it was found that the flexible PSCs can be well attached to varied substrates with PUA, providing a facile route for the attachable PSCs in various scenarios without additional encapsulation and installation.

With the rapid development of science and technology, paper-based functional materials have become the core of the field of new materials. Recently, they have received extensive attention in the field of energy storage due to their advantages of rich and adjustable porous network structure, good flexibility. As an important energy storage device, paper-based supercapacitors have important application prospects in many fields, and have also received extensive attention from researchers in recent years. At present, researchers have modified and regulated paper-based materials by different means such as structural design and material composition to enhance their electrochemical storage capacity. The development of paper-based supercapacitors provides an important direction for the development of green and sustainable energy. Therefore, it is of great significance to summarize the relevant work of paper-based supercapacitors for their rapid development and application. In this review, the recent research progress of paper-based supercapacitors based on cellulose was summarized in terms of various cellulose-based composites, preparation skills and electrochemical performance. Finally, some opinions on the problems in the development of this field and the future development trend were proposed. It is hoped that this review can provide valuable references and ideas for the rapid development of paper-based energy storage devices.

Anode-free Li-metal batteries (AFLBs) are of significant interest to energy storage industries due to their intrinsically high energy. However, the accumulative Li dendrites and dead Li continuously consume active Li during cycling. That results in a short lifetime and low Coulombic efficiency (CE) of AFLBs. Introducing effective electrolyte additives can improve the Li deposition homogeneity and solid-state interphase (SEI) stability for AFLBs. Herein, we reveal that introducing dual additives, composed of LiAsF6 and FEC, into a commercial carbonate electrolyte will boost the cycle life and average CE of NCM||Cu AFLBs. The NCM||Cu AFLBs with the dual additives exhibit a capacity retention of about 75% after 50 cycles, much higher than those with bare electrolytes (35%). The average CE of the NCM||Cu AFLBs with additives can maintain 98.3% over 100 cycles. In contrast, the average CE without additives rapidly decline to 97% after only 50 cycles. In situ Raman measurements reveal that the prepared dual additives facilitate denser and smoother Li morphology during Li deposition. The dual additives significantly suppress the Li dendrite growth, enabling stable SEI formation on anode and cathode surfaces. Our results provide a broad view of developing low-cost and high-effective functional electrolytes for high-energy and long-life AFLBs.

A suitable interface between the electrode and electrolyte is crucial in achieving highly stable electrochemical performance for Li-ion batteries, as facile ionic transport is required. Recently, intriguing research and development have been carried out to form a stable interface between the electrode and electrolyte. Therefore, it is essential to investigate emerging knowledge and contextualize it. The nanoengineering of the electrode-electrolyte interface has been actively researched both at the electrode/electrolyte and interphase levels, which calls for significant attention. This review presents and summarizes some recent advances aimed at nanoengineering approaches to build a more stable electrode-electrolyte interface and assess the impact of each approach adopted. Furthermore, future perspectives on the feasibility and practicality of each approach will also be reviewed in detail. Finally, this review aids in projecting a more sustainable research pathway for a nanoengineered interphase design between electrode and electrolyte, which is pivotal for high-performance, thermally stable Li-ion batteries.

The interfacial contacts between the electron transporting layers (ETLs) and the photoactive layers are crucial to device performance and stability for OSCs with inverted architecture. Herein, atomic layer deposition (ALD) fabricated ultrathin Al2O3 layers are applied to modify the ETLs/active blends (PM6:BTP-BO-4F) interfaces of OSCs, thus improving device performance. The ALD-Al2O3 thin layers on ZnO significantly improved its surface morphology, which led to the decreased work function of ZnO and reduced recombination losses in devices. The simultaneous increase in open-circuit voltage (), short-circuit current density () and fill factor (FF) were achieved for the OSCs incorporated with ALD-Al2O3 interlayers of a certain thickness, which produced a maximum PCE of 16.61%. Moreover, the ALD-Al2O3 interlayers had significantly enhanced device stability by suppressing degradation of the photoactive layers induced by the photocatalytic activity of ZnO and passivating surface defects of ZnO that may play the role of active sites for the adsorption of oxygen and moisture.